ELEGOO Rapid PLA+ filamentas (pilkas)

Rapid PLA+ ELEGOO Filament (gray)

Rapid PLA+ (polylactide plus - a biodegradable material of plant origin, enriched with additives to increase durability) ELEGOO in gray variant is a filament designed for fast, technical prints. The subdued color masks minor imperfections and allows you to focus on the shape of the model. The material works well in utility projects, prototypes and structural elements where precision and repeatability are important. The spool holds 1 kg of plastic.

Performance at high speeds

The filament melts quickly and flows smoothly out of the nozzle, allowing you to print at speeds of up to 600 mm/s (with a properly adjusted printer). Rapid PLA+ has better flexibility and crack resistance compared to standard PLA, making prints less brittle and more durable. In addition, it conducts heat well, which promotes layer bonding.

Accuracy and convenience

A diameter of 1.75 mm and a dimensional tolerance of ± 0.02 mm ensure even feeding of the material and reduce the risk of nozzle clogging. The plastic is wound by machine and then checked by hand, reducing entanglements. The recycled cardboard spool makes segregation easy, and the whole thing is vacuum-packed with a moisture absorber - so the material is ready for printing as soon as it is opened.

General

ManufacturerELEGOOModel50.203.0116ColorGrayWeight1 kg

Recommended print settings

Drying before printing55 ± 5°CAmbient temperature and humidity≤ 50°C, ≤ 20% relative humidity (store with moisture absorber)Nozzle temperature200 - 230°CTable temperature (depending on printer and surface)35 - 65°CType of working surfaceTextured PEI (polyetherimide - a durable material that holds prints well) or other compatible platesPrinting speedLess than 600 mm/sec

Physical properties

Density1.23 g/cm³Melting point160°CDeflection temperature under load57°CSoftening temperature (Vicat test)62°C

Mechanical properties

Tensile strength (XY - measured in the horizontal plane of the print, where the material is strongest)39 ± 2 MPaElongation at break (XY)8,5% ± 1,2%Bending strength (XY)71 ± 6 MPaBending modulus (XY)2846 ± 175 MPaImpact strength (XY)50.4 ± 2.8 kJ/m²