AnyCubic PLA Filament 1,75 mm, 1kg, Pilkas

Anycubic Filament 1.75 mm – Reliable and Eco-Friendly Material for 3D Printing

Product Description:
Anycubic filament with a diameter of 1.75 mm (±0.02 mm) is designed for high precision and reliability during printing.
With a density of 1.24 g/cm3 and a melt index of 4–10 min (190 °C / 2.16 kg), it offers excellent stability throughout the printing process.
An integrated RFID chip enables automatic material color recognition on compatible printers.
The filament is tightly wound to minimize the risk of tangling during printing. It is completely bubble-free, ensuring smooth extrusion and preventing nozzle clogs.
Additionally, it is made from environmentally friendly material, making it safe for the environment.

Key Printing Properties:
Recommended printing temperature: 190–230 °C
Recommended bed temperature: 55–65 °C
Recommended printing speed: 50–200 mm/s
Cooling time: approximately 8 seconds
Maximum extrusion volume: up to 12 mm3/s
These parameters make the filament suitable for a wide range of projects, from detailed prototypes to functional parts printed at higher speeds.

Storage and Maintenance:
To maintain optimal filament performance, it is recommended to:

Dry at 45–50 °C
Drying time: 6–8 hours
Use a nozzle with a diameter of 0.4 mm or larger
Proper care ensures consistent results and longer material lifespan.


Specifications:
Filament diameter: 1.75 mm (±0.02 mm)
Filament density: 1.24 g/cm3
Melt index: 4–10 min (190 °C / 2.16 kg)
RFID chip for color recognition
Tightly wound to reduce tangling
Bubble-free
Prevents nozzle clogging
Made from eco-friendly material
Printing Parameters:

Spool Parameters
Outer Diameter: 195mm
Height (Width): 58mm
Hole Diameter (Center): 73mm
Empty Spool Weight: 127g
Filament Weight: 1kg

Recommended printing temperature: 190–230 °C
Recommended bed temperature: 55–65 °C
Recommended print speed: 50–200 mm/s
Cooling time: 8 seconds
Maximum print volume: 12 mm3/s
Storage and Maintenance:

Recommended drying temperature: 45–50 °C
Recommended drying time: 6–8 hours
Recommended nozzle diameter: 0.4 mm and above